| About |
|---|
| Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no mold release.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Steam sterilized,Biocompatible,Ethylene oxide disinfection |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | g/cm³ | ASTM D792 | |
| — | 1.19 | g/cm³ | ISO 1183 |
| Specific volume | 0.830 | cm³/g | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 18 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 16.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| Equilibrium, 100 ℃ | 0.58 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 690 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 3200 | J/m | ASTM D4812 |
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 62.0 | J | ASTM D3763 |
| Drop hammer impact | |||
| 23℃ | 169 | J | ASTM D3029 |
| Tensile impact strength | 546 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 137 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 129 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 122 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| — | 154 | ℃ | ASTM D1525 12 |
| B50 | 140 | ℃ | ISO 306 |
| B120 | 141 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| specific heat | 1250 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | |||
| — | 0.19 | W/m/K | ASTM C177 |
| — | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| — | > 1.0E+17 | ohms·cm | ASTM D257 |
| — | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in air | 15 | kV/mm | ASTM D149 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 60 Hz | 3.17 | ASTM D150 | |
| 50 kHz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | |||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 25 | % | ASTM D2863 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542 | |
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 70 | ||
| R-level | 118 | ||
| Tensile modulus | |||
| — | 2370 | MPa | ASTM D638 |
| — | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 62.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| fracture | 68.0 | MPa | ASTM D638 |
| fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 100 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span | 96.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Injection instructions | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 295 | °C | |
| Barrel front temperature | 280 to 305 | °C | |
| Nozzle temperature | 275 to 300 | °C | |
| Processing (melt) temperature | 280 to 305 | °C | |
| Mold temperature | 70 to 95 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. Type S |
| 10. 120*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 12. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |