LEXAN™ HP3NREU resin

About
LEXAN™ HP3NREU是一种无定形的,中等流动性的聚碳酸酯(PC)，由沙特基础工业公司提供。具有生物相容性、埃托奥和蒸汽灭菌，不含内部脱模。具有优异的机械、光学、电气和热性能。适合注塑加工。用于医疗器械和药物应用。符合ISO10993或USP VI等级。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Excellent Processability,Ductility,Internal mold release
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	63	MPa	ISO 527
Fracture, 50 mm/min	70	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	6	%	ISO 527
Fracture, 50 mm/min	110	%	ISO 527
Tensile modulus
1 mm/min	2350	MPa	ISO 527
bending strength
Yield, 2 mm/min	90	MPa	ISO 178
Bending modulus
2 mm/mim	2300	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	810	J/m	ASTM D256
-30℃	100	J/m	ASTM D256
Total energy of instrument impact
23℃	642	cm-kgf	ASTM D 3763
Notched impact strength of cantilever beam
23℃，80103	NB	kJ/m²	ISO 180/1U
-30℃，80103	NB	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
23℃，80103	70	kJ/m²	ISO 180-1A
-30℃，80103	10	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
80103
80103
23℃	70	kJ/m²	ISO 180/1A
-30℃	15	kJ/m²	ISO 180/1A
23℃	NB	kJ/m²	ISO 179/1eU
-30℃	NB	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	141	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, 64 mm span	125	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	132	℃	ASTM D648
Linear coefficient of thermal expansion
MD：-40~95℃	6.84E-0.5	1/℃	ASTM E831
TD：-40~95℃	6.84E-0.5	1/℃	ASTM E831
Linear coefficient of thermal expansion
MD：23~80℃	7.E-0.5	1/℃	ISO 11359-2
TD：23~80℃	7.E-0.5	1/℃	ISO 11359-2
Vicat Softening Temp
B50	141	℃	ISO 306
B120	142	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
300℃，1.20kg	14	g/10min	ASTM D1238
Density	1.2	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃	0.35	%	ISO 62
23℃，50% RH	0.15	%	ISO 62
Melt Volume Rate
300℃，1.2 kg	12	cm³/10min	ISO 1133

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	2 – 4	hrs
Maximum water content	0.02	%
Melt temperature	280 – 310	°C
Nozzle temperature	270 – 290	°C
Front Section Zone 3 Temperature	280 – 310	°C
Temperature in Zone 2 of the middle section	270 – 290	°C
Temperature in Zone 1 of the rear section	260 – 290	°C
Hopper temperature	60 – 80	°C
Mold temperature	80 – 110	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.