| About |
|---|
| Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Steam sterilized,Biocompatible,Good stripping performance,Moderate liquidity,Ethylene oxide disinfection,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.50 to 0.70 | % | |
| MD：3.2 mm | 0.50 to 0.70 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.35 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 15 | kJ/m² | ISO 179/1eA |
| 23℃ | 75 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 100 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 63.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 138 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 127 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| — | 141 | ℃ | ASTM D1525 19 |
| B50 | 143 | ℃ | ISO 306 |
| B120 | 145 | ℃ | ISO 306/B120 |
| Ball pressure test | IEC 60695-10-2 | ||
| 125℃ | Pass | ||
| 140℃ | Pass | ||
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| Relative temperature index | 125 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glowing wire flammability index | |||
| 1.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | |||
| 2540 µm | 88.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.80 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 95.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2370 | MPa | ASTM D638 |
| — | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 62.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| fracture | 68.0 | MPa | ASTM D638 |
| fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span | 96.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 280 to 310 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 310 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*3 sp=62mm |
| 9. 80*10*3 mm |
| 10. 120*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 12. Approximate Maximum |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |