| About |
|---|
| 中低流动性聚碳酸酯，用于医疗器械和药物的应用，具有生物相容(ISO10993或USPClass VI). 用于蒸汽、电子束和伽玛灭菌，与HPS6相比，有更高的脱模剂 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Biocompatible |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Fracture, Type I, 50 mm/min | 70 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 135 | % | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 99 | MPa | ASTM D790 |
| Bending modulus | |||
| 0.45 MPa | 137 | ℃ | ASTM D 648 |
| 1.3 mm/min，50mm跨距 | 2390 | MPa | ASTM D790 |
| 1.8MPa | 132 | ℃ | ASTM D 648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 3260 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 920 | J/m | ASTM D256 |
| Instrument impact energy peak | |||
| 23℃ | 67 | N.m | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| Unannealed, 6.4 mm |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.2 | ASTM D792 | |
| Water absorption rate | |||
| 24hr | 0.15 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5 – 0.7 | % | Internal Method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7 | g/10min | ASTM D1238 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | ||
| Drying time | 3 – 4 | hrs | |
| Drying time (cumulative) | 48 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 310 – 330 | °C | |
| Nozzle temperature | 305 – 325 | °C | |
| Front Section Zone 3 Temperature | 310 – 330 | °C | |
| Temperature in Zone 2 of the middle section | 300 – 320 | °C | |
| Temperature in Zone 1 of the rear section | 290 – 310 | °C | |
| Mold temperature | 80 – 115 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shoot to cylinder size | 40 – 60 | % | |
| Depth of exhaust groove | 0.025 – 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |