| About |
|---|
| Medium flow specialty polycarbonate – improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Steam sterilized,Biocompatible,Moderate liquidity,High pressure heat resistance,Ethylene oxide disinfection,HB,V-2 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.40 to 0.80 | % | |
| TD：3.2 mm | 0.40 to 0.80 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.24 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.093 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 800 | J/m | |
| 23℃ | 890 | J/m | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 85.0 | J | |
| 23℃，Total Energy | 82.4 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 124 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 119 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 141 | ℃ | ASTM D1525，ISO 306 |
| B120 | 142 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~95℃ | 7.9E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 7.9E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 130 | ℃ | UL 746 |
| Electrical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | ||
| 2.50 mm | V-2 | ||
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 825 | ℃ | |
| 3 mm | 825 | ℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2540 µm | 82.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | 3.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| Level L | 90 | ASTM D785 | |
| Tensile modulus | |||
| — | 2220 | MPa | ASTM D638 |
| — | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 58.0 | MPa | ASTM D638 |
| yield | 57.9 | MPa | ISO 527-2/50 |
| fracture | 64.1 | MPa | ASTM D638 |
| fracture | 61.5 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.8 | % | ASTM D638 |
| yield | 5.5 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2220 | MPa | ASTM D790 |
| — | 2150 | MPa | ISO 178 |
| bending strength | |||
| — | 90.2 | MPa | ISO 178 |
| Yield, 50 mm span | 94.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 mm |
| 8. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |