| About |
|---|
| Global grade. LEXAN LUX2010T is an injection moulding grade especially designed for manufacturing optical parts requiring excellent flow properties combined with very high transmission and color stability.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Good color stability |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 38 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 to 0.90 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 62.0 | MPa | |
| fracture | 63.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 7.0 | % | |
| fracture | 130 | % | |
| Bending modulus | |||
| 50 mm span | 2360 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 98.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 80 | J/m | |
| 23℃ | 670 | J/m | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 2100 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 63.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 139 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 127 | ℃ | |
| Vicat Softening Temp | |||
| B120 | 143 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~95℃ | 6.4E-5 | 1/℃ | |
| TD：-40~95℃ | 6.7E-5 | 1/℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 2540 µm | > 90.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 48 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |