| About |
|---|
| LEXAN™树脂ML4539是一种无定形，不透明的聚碳酸酯。具有高机械，光学，电气和热性能。提供抗冲击性和出色的尺寸稳定性。通过注射成型加工，用于飞机机舱和货舱应用。要求符合FAR 25.853a标准 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Yield, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 90 | % | ASTM D638 |
| Yield, Type I, 50 mm/min | 7 | % | ASTM D638 |
| bending strength | |||
| Yield, 1.30 mm/min, 50 mm span | 90.252 | MPa | ASTM D790 |
| Bending modulus | |||
| Fracture, 1.30 mm/min, 50 mm span | 2236.68 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 3194.8 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 637 | J/m | ASTM D256 |
| Tensile impact | |||
| S-shaped | 535 | cm-kgf/cm² | ASTM D 1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.21 | ASTM D792 | |
| Specific volume | 0.83 | cm³/g | ASTM D 792 |
| Water absorption for 24 hours | 0.15 | % | ASTM D 570 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5 – 0.7 | % | ASTM D570 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 9 | g/10min | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FAA flame retardant rating, FAR 25.853 A/BFAA flame retardant rating, FAR 25.853 A/B | 通行证 | FAR 25.853 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3 – 4 | hrs | |
| Drying time (cumulative) | 48 | hrs | |
| Maximum water content | 0.02 | % | |
| Melt temperature | 295 – 315 | °C | |
| Nozzle temperature | 290 – 310 | °C | |
| Temperature in the first three zones | 295 – 315 | °C | |
| Middle Zone 2 Temperature | 280 – 305 | °C | |
| Rear – Zone 1 Temperature | 270 – 295 | °C | |
| Mold temperature | 70 – 95 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 40 – 70 | rpm | |
| Shoot to cylinder size | 40 – 60 | % | |
| Depth of exhaust groove | 0.025-0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |