| About |
|---|
| Optical quality, high purity PC resin for CD/DVD and BD applications at short cycle times&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High purity,Optical performance,Quick molding cycle |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，1.2 kg | 9.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2350 | MPa | ASTM D638 |
| — | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| fracture | 60.0 | MPa | ASTM D638 |
| fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | > 40 | % | ASTM D638 |
| fracture | > 40 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2300 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 132 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 122 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 122 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 138 | ℃ | ASTM D1525, ISO 306/B50 10 15 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.010 | IEC 60250 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | |||
| 2540 µm | > 90.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.70 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 270 to 290 | °C | |
| Barrel middle temperature | 320 to 340 | °C | |
| Barrel front temperature | 350 to 380 | °C | |
| Nozzle temperature | 340 to 370 | °C | |
| Processing (melt) temperature | 340 to 370 | °C | |
| Mold temperature | 75.0 to 95.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*3 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |