| About |
|---|
| Lexan* RCX7243 is an impact modified PC blend containing 30% PCR content with non-brominated and non-chlorinated FR for thin-wall applications requiring excellent impact/flow balance performance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,Flame Characteristics,V-2,V-1,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.15 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| yield | 58.0 | MPa | |
| fracture | 53.0 | MPa | |
| Tensile strain | ASTM D638 | ||
| yield | 4.0 | % | |
| fracture | 60 | % | |
| Bending modulus | |||
| 50 mm span | 2350 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 130 | J/m | ASTM D256 |
| 23℃ | 690 | J/m | ASTM D256 |
| 23℃ | 50 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 57.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 101 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 86.0 | ℃ | |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 7 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 7.5E-5 | 1/℃ | |
| TD：-40~40℃ | 7.5E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.40 mm | V-2 | ||
| 0.60 mm | V-1 | ||
| 0.75 mm | V-0 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 230 to 280 | °C | |
| Barrel middle temperature | 240 to 290 | °C | |
| Barrel front temperature | 250 to 300 | °C | |
| Nozzle temperature | 250 to 300 | °C | |
| Processing (melt) temperature | 250 to 300 | °C | |
| Mold temperature | 60.0 to 85.0 | °C | |
| Vent depth | 0.030 to 0.075 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |