| About |
|---|
| XHT1171 is an 85 MVR high flow, high heat polycarbonate copolymer enabling high aesthetics, thin wall and complex designs. It is available in a range of opaque colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Negative |
| Features | High liquidity,High Heat Resistance,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | ASTM D1238 | ||
| 300℃，2.16kg | 37 | g/10min | ASTM D1238 |
| 330℃，2.16kg | 90 | g/10min | ASTM D1238 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，2.16 kg | 33.0 | cm³/10min | ISO 1133 |
| 330℃，2.16 kg | 85.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.90 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.25 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 75 | J/m | ASTM D256 |
| 23℃ | 80 | J/m | ASTM D256 |
| -30℃ | 9.0 | kJ/m² | ISO 180-1A |
| 23℃ | 9.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ASTM D4812 , ISO 180/1U | ||
| -30℃ | 无断裂 | ASTM D4812 , ISO 180/1U | |
| 23℃ | 无断裂 | ASTM D4812 , ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 150 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 150 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 138 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 138 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 155 156 | ℃ | ASTM D1525 10 |
| B50 | 155 | ℃ | ISO 306 |
| B120 | 158 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ASTM E831 , ISO 11359-2 | ||
| MD：-40~40℃ | 6.0E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| TD：-40~40℃ | 6.0E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| Thermal conductivity coefficient | |||
| 25℃ | 0.20 | W/m/K | ASTM C177 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Metallized Haze（1.50 mm） | 145 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 125 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 145 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2450 | MPa | ASTM D638 |
| — | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 70.0 | MPa | ASTM D638 |
| yield | 70.0 | MPa | ISO 527-2/50 |
| fracture | 60.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 7.0 | % | ASTM D638 |
| yield | 7.0 | % | ISO 527-2/50 |
| fracture | > 25 | % | ASTM D638 |
| fracture | > 55 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2600 | MPa | ASTM D790 |
| — | 2350 | MPa | ISO 178 |
| bending strength | |||
| — | 105 | MPa | ISO 178 |
| Yield, 50 mm span | 110 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*3 sp=62mm |
| 8. 80*10*3 mm |
| 9. 80*10*4 mm |
| 10. Rate A (50°C/h), Loading 2 (50 N) |
| 11. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |