| About |
|---|
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 26 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃，3.2mm | 68.6 | J/m | ASTM D256 |
| -30℃，6.4mm | 58.8 | J/m | ASTM D256 |
| 23℃，3.2mm | 176 | J/m | ASTM D256 |
| 23℃，6.4mm | 147 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 92.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 85.0 | ℃ | |
| Vicat Softening Temp | |||
| B50 | 91.0 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance | 60 | ℃ | UL 746 |
| Impact mechanical performance | 60 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 27 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0,5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 98 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm | 2060 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm | 36.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 3.20 mm | 5 | % | ASTM D638 |
| Fracture, 3.20 mm | 20 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2260 | MPa | ASTM D790 |
| bending strength | |||
| 6.40 mm | 60.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 70-80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 170to 190 | °C | |
| Temperature in the middle of the barrel | 180 to 200 | °C | |
| Front temperature of material barrel | 190 to 210 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 40.0 to 60.0 | °C | |
| Back pressure | 0.49 to 0.98 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |