| About |
|---|
| LG ABS BM662B是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:吹塑成型。 LG ABS BM662B的主要特性为:耐热。 典型应用领域包括: 汽车行业 房屋&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 2.0 | g/10min | ISO 1133 |
| 220℃，10.0kg | 2.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ISO 294-4 |
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 69 | J/m | ASTM D256 |
| -30℃，6.4mm | 59 | J/m | ASTM D256 |
| 23℃，3.2mm | 160 | J/m | ASTM D256 |
| 23℃，6.4mm | 160 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 103 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 93.0 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 6.4 mm | 110 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 4.0 mm | 100 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 6 |
| B50 | 110 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：23~60℃ | 8.0E-5 to 9.0E-5 | 1/℃ | ISO 11359-2 |
| MD：23~60℃ | 8.0E-5 to 9.0E-5 | 1/℃ | ISO 11359-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 3.20 mm | 46.1 | MPa | ASTM D638 |
| yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 3.20 mm | 15 | % | ASTM D638 |
| Bending modulus | 1950 | MPa | ISO 178 |
| 3.20 mm | 2060 | MPa | ASTM D790 |
| bending strength | 72.0 | MPa | ISO 178 |
| 3.20 mm | 69.6 | MPa | ASTM D790 |
| Rockwell hardness | 100 | ISO 2039-2 | |
| R-level | 100 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Connector temperature | 220 | °C | |
| Melt temperature | 200 to 230 | °C | |
| Nozzle temperature | 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |