| About |
|---|
| Description Well balanced mechanical properties Application Electric/electronic products, miscellaneous goods&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 21 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| dimensional stability | 0.0 | % | ASTM D1042 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 130 | J/m | |
| -30℃，6.4mm | 130 | J/m | |
| 23℃，3.2mm | 340 | J/m | |
| 23℃，6.4mm | 310 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 91.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 87.0 | ℃ | |
| Vicat Softening Temp | 93.0 | ℃ | ASTM D1525 6 |
| 1.50 mm | 95.0 | ℃ | |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 3.00 mm | 100 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 27 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 1 | ||
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 108 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm | 2080 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm | 45.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 40 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2450 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 72.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 200 to 220 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 210 to 240 | °C | |
| Mold temperature | 40.0 to 70.0 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2,0 in/min |
| 3. 0,59 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |