| About |
|---|
| Description General Purpose, Low Gloss Application Automotive Sheet, Semi-Conductor Tray&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Low Gloss,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.19 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，3.2mm | 69 | J/m | |
| -20℃，6.4mm | 59 | J/m | |
| 23℃，3.2mm | 98 | J/m | |
| 23℃，6.4mm | 69 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 91.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 99.0 | ℃ | ASTM D1525 6 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | ||
| 1.60 mm | HB | ||
| 2.50 mm | HB | ||
| 3.20 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 47.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | > 60 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2350 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 70.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70.0 to 80.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 210 | °C | |
| Barrel front temperature | 200 to 230 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 40.0 to 60.0 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Drying temperature | 70.0 to 80.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.010 | % | |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 200 to 230 | °C | |
| Barrel 4 zone temperature | 200 to 230 | °C | |
| Connector temperature | 200 to 230 | °C | |
| Melt temperature | 200 to 230 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |