| About |
|---|
| Description High Flow, Metal Plating Application Decorative Parts (Home Appliance Door Handle Etc)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High liquidity,Electroplating |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.55 | % | ASTM D995 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 27.00 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 87 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 95 | ℃ | ASTM D1525 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 30 | KV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 340 | J/m | ASTM D256 |
| -30℃ | 160 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 105 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 43.1 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 40 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 70.6 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2350 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Drying temperature | 70 -80 | °C | |
| Drying time | 3.0-4.0 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 190-210 | °C | |
| Central temperature of the barrel | 200-220 | °C | |
| Barrel front temperature | 210-230 | °C | |
| Die temperature | 210-230 | °C | |
| Mold temperature | 40-60 | °C | |
| Drying temperature | 70-80 | °C | |
| Drying time | 3.0-4.0 | Hr | |
| Zone 1 temperature | 180-200 | °C | |
| Zone 3 temperature | 200-230 | °C | |
| Die temperature | 220-230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |