| About |
|---|
| Description High Heat ASA Application Automotive Part (Radiator Grill, Side Mirror)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Material Status | Commercial: Active |
| Features | HB,High Heat Resistance |
| Availabilitys | North America,Europe,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 6.0 | g/10min | ISO 1133 |
| 220℃，10.0kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.70 | % | ASTM D955 |
| MD：3.2 mm | 0.40 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | |||
| 23℃，6.4mm | 140 | J/m | ASTM D256 |
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed, 6.4 mm | 94.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 88.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temperature | 102 | ℃ | ASTM D1525 6 |
| B50 | 102 | ℃ | ISO 306 |
| Relative Temperature Index (RTI) | |||
| Electrical performance Elec | 50.0 | ℃ | UL 746 |
| Impact mechanical performance Tmp | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| Yield yld, 3.20 mm | 47.1 | MPa | ASTM D638 |
| Yield yld | 48.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Broken BRK, 3.20 mm | 20 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| 6.40 mm | 2300 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ISO 178 |
| 6.40 mm | 75.5 | MPa | ASTM D790 |
| Rockwell hardness | 104 | ISO 2039-2 | |
| R-level | 104 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 70 to 80 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature Zone 1 | 200 to 220 | °C | |
| Middle Temperature Zone 2 | 210 to 230 | °C | |
| Front Temperature Zone 3 | 220 to 240 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Melt Temperature | 190 to 210 | °C | |
| Mold Temperature | 40 to 60 | °C | |
| Back Pressure | 0.981 to 2.94 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. 0.079 in/min |
| 5. 120*10*4mm |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |