| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | Renewable resources,Good Rigidity,Environmental protection,weathering resistance,high wear resistance ,high machine finish |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Mold Shrinkage | 0.2-0.6 | % | ASTM D955 |
| Water Absorption | 0.3 | % | ASTM D570 |
| Melt Flow Rate | |||
| 230ºC/3.8kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M Scale | 95 | ISO 2039-2 | |
| 124 | R Scale | ISO 2039-2 | |
| Tensile Strength | |||
| 5mm/min | 74 | MPa | ISO 527-2 |
| Elongation at Break | |||
| 5mm/min | 5.0 | % | ISO 527 |
| Tensile Modulus | |||
| 1mm/min | 3200 | MPa | ISO 527-2 |
| Flexural Strength | |||
| 2mm/min | 111 | MPa | ISO 178 |
| Flexural Modulus | |||
| 2mm/min | 3000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notch Impact strength | 1.5 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| B/50 | 108 | ℃ | ISO 306/B |
| Hot deformation temperature HDT | |||
| 1.8 MPa | 101 | ℃ | ISO 75 |
| Coeff. of linear thermal expansion | 6 | ×10-5/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.5 mm | HB | calss | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| Drying Temperature | 80-90 | ℃ | |
| Drying Time | 4-6 | hr | |
| Melt Temperature | 220-250 | ℃ | |
| Mold Temperature | 60-80 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |