| Description Flame Retardant Application Electric Parts Requring Flame Retardancy&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 26.5 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | > 5.0 | % | |
| fracture | 60 | % | |
| Bending modulus | 2160 | MPa | ASTM D790 |
| bending strength | 39.2 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃，3.2mm | 49 | J/m | |
| -30℃，6.4mm | 39 | J/m | |
| 23℃，3.2mm | 130 | J/m | |
| 23℃，6.4mm | 88 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 87.0 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 81.0 | ℃ | |
| Vicat Softening Temp | 84.0 | ℃ | ASTM D1525 5 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 70 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.010 | % | |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 190 to 200 | °C | |
| Barrel front temperature | 200 to 210 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.59 in/min |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |