| LG PS 50IS是一种高抗冲聚苯乙烯材料,。 该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,。 LG PS 50IS的主要特性为:阻燃/额定火焰。 典型应用领域包括: 薄板 电影 容器 生活消费品&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 200℃，5.0kg | 8.0 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 80 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 19 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.80 | % | ASTM D955 |
| dimensional stability | 0.0 | % | ASTM D1042 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 59 | J/m | ASTM D256 |
| -30℃，6.4mm | 49 | J/m | ASTM D256 |
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| 23℃，6.4mm | 78 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 80.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 88.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 87.0 | ℃ | ASTM D1525 5 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 1.5 mm | 50.0 | ℃ | UL 746 |
| 3.0 mm | 50.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 44 | kV/mm | ASTM D149 |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.5 mm | PLC 4 | UL 746 | |
| 3.0 mm | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm | 1770 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm | 26.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 59 | % | ASTM D638 |
| Yield, 3.20 mm | 5.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2160 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 3.20 mm | 42.2 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 99 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |