Lifoflex® UVX 56.01 B038-3

About
There are many advantages in using polyamide (PA) in an application, including high temperature resistance, a very high strength, a matt surface and excellent stiffness and impact resistance. When combined with Lifoflex PA bonding grades, you get the properties of both materials in one product. These special TPE grades offer excellent bonding to PA6, PA66, PA12 in two component applications. Giving you the advantage of soft-touch qualities without the need for separate primer or adhesive. A high bonding strength is also possible to glass fibre reinforced polyamide materials (up to 40% glass fibre). The outstanding properties of these TPE compounds, such as high service temperature range, high oil resistance, soft touch surface and high flexibility, open up the design possibilities in a wide variety of applications. The Lifoflex PA bonding grades are very easy to process via injection moulding. The wide processing window results in a lower rate of defective parts and faster cycle times.&&

About

There are many advantages in using polyamide (PA) in an application, including high temperature resistance, a very high strength, a matt surface and excellent stiffness and impact resistance. When combined with Lifoflex PA bonding grades, you get the properties of both materials in one product. These special TPE grades offer excellent bonding to PA6, PA66, PA12 in two component applications. Giving you the advantage of soft-touch qualities without the need for separate primer or adhesive. A high bonding strength is also possible to glass fibre reinforced polyamide materials (up to 40% glass fibre). The outstanding properties of these TPE compounds, such as high service temperature range, high oil resistance, soft touch surface and high flexibility, open up the design possibilities in a wide variety of applications. The Lifoflex PA bonding grades are very easy to process via injection moulding. The wide processing window results in a lower rate of defective parts and faster cycle times.&&

Product Description
Generic	TPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good flexibility,High impact resistance,Quick molding cycle,High Heat Resistance,Grease resistance,Solvent resistance,Agglomerability
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.09	g/cm³	ISO 1183
Melt Flow Rate
230℃，5.0kg	4.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	56		DIN 53505

elastic body	Nominal value	Unit	Test method
tensile strength
Flow rate, yield	5.10	MPa	DIN 53504
Tensile strain
Flow rate, fracture	530	%	DIN 53504
Compression deformation			ISO 815
23℃，22 hr	12	%	ISO 815
70℃，22 hr	32	%	ISO 815
110℃，24 hr	56	%	ISO 815

Supplementary information	Nominal value	Unit	Test method
Oil absorption capacity
70℃	15	%

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	240 to 260	°C
Mold temperature	20 to 60	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. 72 hr, Motor Oil 5W-30 fully synthetic
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.