LIHAN® CT100 - SOLIAO

About
LIHAN® CT100 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated.&&

Product Description
Supplier	Lihan
Generic	PC+PBT
Material Status	Commercial: Active
Features	HB
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.21	g/cm³	ISO 1183
Shrinkage rate	0.60 to 1.0	%
water content	0.20	%	ISO 62

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	70	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	125	℃	ISO 75-2/B
1.8 MPa, unannealed	90.0	℃	ISO 75-2/A

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms	ASTM D257
Dielectric strength	17	kV/mm	ASTM D149

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	115		ISO 2039-2
tensile strength
fracture	50.0	MPa	ISO 527-2
Tensile strain
fracture	85	%	ISO 527-2
Bending modulus	2360	MPa	ISO 178
bending strength	85.0	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	240 to 275	°C
Mold temperature	40 to 80	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.