| About |
|---|
| LINATHENE LL120 is a butene linear low density polyethylene (LLDPE) developed for tubular blown film or slot cast film extrusion. Films made from LINATHENE LL120 have excellent toughness, tensile strength, elongation, puncture strength. LINATHENE LL120 is recommended for the manufacture of prime liner film, garment bag, freezing bag and other industrial and consumer packaging applications.&& |
| Product Description | |
|---|---|
| Supplier | USI |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good dissection,Food contact compliance,Inoxidizability,Good Tensile Strength,Low density,Puncture Resistant |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | 2.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield | 11.3 | MPa | ASTM D882 |
| TD, yield | 9.81 | MPa | ASTM D882 |
| MD, fracture | 24.5 | MPa | ASTM D882 |
| TD, fracture | 17.7 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 450 | % | ASTM D882 |
| TD, fracture | 550 | % | ASTM D882 |
| Drop hammer impact | 110 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 103 | ℃ | ASTM D1525 |
| Melting peak temperature | 122 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |