| Lion Idemitsu Composites PPS T541M1 is a Polyphenylene Sulfide (PPS) product filled with 60% carbonmineral. It is available in Asia Pacific. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Lion Idemitsu |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Lubricating,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 | % | ISO 294-4 |
| MD | 0.15 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | > 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 4.3 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 269 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 4.0E-6 | 1/℃ | ISO 11359-2 |
| TD | 2.4E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Flowability（1.00 mm） | 8.00 | cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 102 | ISO 2039-2 | |
| tensile strength | 160 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.60 | % | ISO 527-2 |
| Bending modulus | 35800 | MPa | ISO 178 |
| bending strength | 295 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Internal Method |
| 3. Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |