| About |
|---|
| Liten FB 75 is a high-density polyethylene produced by Unipetrol RPA using UNIPOL gas-phase technology. Characteristics: C6 – copolymer semi-HMW PE natural pellets meets European Pharmacopoeia 8: (Ph.Eur. 8, 3.1.3) International designation: ISO 17855-PE-HD,F,50-T006 Application: blown films above 7 µm food packaging and freezing shopping bags&& |
| Product Description | |
|---|---|
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Food contact compliance,Copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.10 | g/10min | ISO 1133 |
| 190℃，21.6kg | 12 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.55 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 2000 | hr | ASTM D1693 |
| Full incision creep test | ISO 16770 | ||
| （4 MPa，2%）：80℃ | 1.3 | day | ISO 16770 |
| （9 MPa，2%）：50℃ | 2.1 | day | ISO 16770 |
| Melt flow ratio | |||
| 21，6/2，16 | 130 | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 60 | ISO 868 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| MD, fracture, 30 µ m | 38.0 | MPa | ISO 527-3 |
| TD, fracture, 30 µ m | 30.0 | MPa | ISO 527-3 |
| Drop hammer impact | |||
| 25 µm | 130 | g | ISO 7765-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 44.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 124 | ℃ | ISO 306 |
| Melting temperature | 128 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blown Film Melt Temperature | 200 to 220 | ℃ | |
| Blow（up Ratio） | >3.7:1.0 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (100%) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |