| About |
|---|
| Liten MB 68 is a high-density polyethylene produced by Unipetrol RPA using UNIPOL gas-phase technology. Characteristics: C6 – copolymer narrow MWD increased processing stability natural pellets International designation: ISO 17855-PE-HD,M,57-D090 Application: cartridges for adhesives technical parts&& |
| Product Description | |
|---|---|
| Generic | LPE Copolymer |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,Weight distribution,Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 7.5 | g/10min | ISO 1133 |
| 190℃，5.0kg | 22 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 2.0 | % | ISO 294-4 |
| MD | 2.3 | % | ISO 294-4 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 55 ℃，F50 | 5.00 | hr | ISO 22088 |
| Melt flow ratio | |||
| 21，6/2，16 | 25.0 | ||
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 5.5 | kJ/m² | ISO 179 |
| 23℃ | 6.5 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 43.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 125 | ℃ | ISO 306 |
| Melting temperature | 134 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 58 | ISO 868 | |
| Tensile modulus | 1050 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 23.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 9.5 | % | ISO 527-2 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 485 | MPa | ISO 899-1 |
| 1000 hr | 275 | MPa | ISO 899-1 |
| Bending modulus | 950 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 290 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (6 MPa; 10%) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |