| About |
|---|
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Negative |
| Features | Optical performance,Inoxidizability,Good heat sealing |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| Density | |||
| 23℃ | 0.918 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| yield | 12 | MPa | ISO 527-2 |
| fracture | 18 | MPa | ISO 527-2 |
| Yield, MD, 25 µ m | 11 | MPa | ISO 527-3 |
| Yield, TD, 25 µ m | 11 | MPa | ISO 527-3 |
| Fracture, MD, 25 µ m | 45 | MPa | ISO 527-3 |
| Fracture, TD, 25 µ m | 40 | MPa | ISO 527-3 |
| nominal strain | |||
| fracture | 740 | % | ISO 527-2 |
| Fracture, MD, 25 µ m | 750 | % | ISO 527-3 |
| Fracture, TD, 25 µ m | 900 | % | ISO 527-3 |
| Opening strength | |||
| 25µm | 80 | g | ASTM D3354 |
| tear strength | |||
| MD，25µm | 1.4 | N | ISO 6383-2 |
| TD，25µm | 2.4 | N | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Drop hammer impact strength | |||
| 25µm | 85 | g | ISO 7765-1 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 50 | % | ASTM D2457 |
| Haze | 11 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 123 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | 97 | ℃ | ISO 306 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |