| About |
|---|
| LNP COLORCOMP A1000H is an unfilled compound based on ABS. Added feature of this grade is: Healthcare. Also known as: LNP* COLORCOMP* Compound A-1000 EES HC Product reorder name: A1000H&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2280 | MPa | ASTM D638 |
| Tensile modulus | 2530 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 33.8 | MPa | ASTM D638 |
| fracture | 35.3 | MPa | ISO 527-2/5 |
| yield | 50.0 | MPa | ISO 527-2/5 |
| yield | 44.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 24 | % | ASTM D638 |
| fracture | 25 | % | ISO 527-2/5 |
| yield | 2.0 | % | ASTM D638 |
| yield | 2.6 | % | ISO 527-2/5 |
| Bending modulus | 2410 | MPa | ISO 178 |
| 50 mm span | 2340 | MPa | ASTM D790 |
| bending strength | 76.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 72.4 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 19 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 130 | J/m | ASTM D256 |
| 23℃ | 320 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.5 | kJ/m² | ISO 180-1A |
| 23℃ | 23 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 31.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 80.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 80.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 94.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 98.0 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 100 | ℃ | ISO 306 |
| B120 | 100 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 8.8E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 8.8E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 8.8E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 8.8E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Strength mechanical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 5.6 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 19 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，5 kg | 14.7 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 240℃，1000 sec^-1 | 230 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 to 0.10 | % | |
| Barrel rear temperature | 182 to 193 | °C | |
| Barrel middle temperature | 193 to 204 | °C | |
| Barrel front temperature | 204 to 216 | °C | |
| Processing (melt) temperature | 199 to 210 | °C | |
| Mold temperature | 10 to 49 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |