| About |
|---|
| LNP* COLORCOMP* C1200HFC is a compound based on PC+ABS. Added features of this grade include: Excellent Flow, Impact, High Heat Resistance, Low Temperature Ductility. For use in automotive, appliance and electrical components.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Negative |
| Features | High impact resistance,High liquidity,Ductility,High Heat Resistance,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 19 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 24.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2280 | MPa | ASTM D638 |
| — | 2370 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 57.2 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| yield | 4.8 | % | ISO 527-2/50 |
| fracture | 150 | % | ASTM D638 |
| fracture | 110 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2340 | MPa | ASTM D790 |
| — | 2250 | MPa | ISO 178 |
| bending strength | |||
| — | 86.0 | MPa | ISO 178 |
| Yield, 50 mm span | 88.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃ | 480 | J/m | ASTM D256 |
| 23℃ | 590 | J/m | ASTM D256 |
| -30℃ | 34 | kJ/m² | ISO 180-1A |
| 23℃ | 49 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Total Energy | 54.2 | J | ASTM D3763 |
| 23℃，Total Energy | 54.2 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 129 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 130 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 113 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 110 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.2E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | 105 | ℃ | UL 746 |
| Electrical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.20 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 80*10*4 mm, Cut |
| 6. 80*10*4 mm |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |