| About |
|---|
| LNP* COLORCOMP* E1000CE is an unfilled custom color compound based on PEI resin. Added features of this grade include: Easy Molding, UV Stabilized, Clean Compound System.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,Excellent Processability,V-0,5VA |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 18 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.25 | % | ASTM D570 |
| Equilibrium, 23 ℃ | 1.3 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 32 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 1300 | J/m | ASTM D4812 |
| Drop hammer impact | |||
| 23℃ | 33.9 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 207 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 199 | ℃ | ASTM D648 |
| Vicat Softening Temp | 219 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD：-20~150℃ | 5.6E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.22 | W/m/K | ASTM C177 |
| Relative temperature index | 170 | ℃ | UL 746 |
| Electrical performance | 170 | ℃ | UL 746 |
| Impact mechanical performance | 170 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 1.6 mm in air | 33 | kV/mm | ASTM D149 |
| 1.6 mm in oil | 28 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 kHz | 3.15 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 2.45 GHz | 2.5E-3 | ASTM D150 | |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Extreme oxygen index | 44 | % | ASTM D2863 |
| NBS smoke density | |||
| Flaming，Ds，4 min | 2.00 | ASTM E662 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 109 | ASTM D785 | |
| Tensile modulus | 3590 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 110 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 7.0 | % | ASTM D638 |
| fracture | 60 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 3520 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 165 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 10.0 | mg | ASTM D1044 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.10 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Tungsten Electrode |
| 7. Surface |
| 8. 4 min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |