| About |
|---|
| LNP COLORCOMP J1000AE is an unfilled Polyethersulfone. Added feature of this grade is: Easy Molding.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | Excellent Processability,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，50% RH | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2690 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 88.9 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 6.5 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 2620 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 50 mm span | 125 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 200 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 5.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.8E+15 | ohms·cm | ASTM D257 |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 1.7E-3 | ASTM D150 | |
| 60 Hz | 1.7E-3 | ASTM D150 | |
| 1 kHz | 2.2E-3 | ASTM D150 | |
| 1 MHz | 5.6E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Barrel rear temperature | 343 to 354 | °C | |
| Barrel middle temperature | 360 to 371 | °C | |
| Barrel front temperature | 371 to 382 | °C | |
| Processing (melt) temperature | 354 to 371 | °C | |
| Mold temperature | 138 to 149 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |