LNP™ ELCRES™ XD2322

About

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	High impact resistance,Flame Characteristics

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile stress
Yield 50 mm/min	58	MPa	ASTM D638
Fracture 50 mm/min	59	MPa	ASTM D638
Yield 50 mm/min	56	MPa	ISO 527
Fracture 50 mm/min	57	MPa	ISO 527
Tensile strain
Yield 50 mm/min	6	%	ASTM D638
Fracture 50 mm/min	112	%	ASTM D638
Yield 50 mm/min	6	%	ISO 527
Fracture 50 mm/min	108	%	ISO 527
Tensile modulus
5 mm/min	2100	MPa	ASTM D638
1 mm/min	2000	MPa	ISO 527
bending strength
1.3 mm/min, 50 mm span	92	MPa	ASTM D790
2 mm/min	87	MPa	ISO 178
Bending modulus
1.3 mm/min, 50 mm span	2400	MPa	ASTM D790
2 mm/min	2100	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23°C	780	J/m	ASTM D256
-30°C	652	J/m	ASTM D256
-40°C	360	J/m	ASTM D256
Total energy of instrument impact
23°C	66	J	ASTM D3763
Notched impact strength of cantilever beam
80103 +23°C	NB	KJ/m²	ISO 180/1U
80103 -30°C	NB	KJ/m²	ISO 180/1U
80103 +23°C	63	KJ/m²	ISO 180/1A
80103 -30°C	29	KJ/m²	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Relative temperature index
Electrical characteristics	1.19		ASTM D792
Mechanical impact performance	0.4 – 0.8	%	SABIC method
Non mechanical impact performance	0.4 – 0.8	%	SABIC method

PHYSICAL	Nominal value	Unit	Test method
Melt Volume Rate
300°C/1.2 kgf	16	g/10 min	ASTM D1238
Density	1.19	g/cm³	ISO 1183
Water absorption rate
23°C	0.4	%	ISO 62-1
Hygroscopicity
23°C/50% RH	0.15	%	ISO 62-4
Melt Flow Rate
300°C/1.2 kg	15	cm³/10 min	ISO 1133

Electrical performance	Nominal value	Unit	Test method
Hot wire ignition (HWI)
PLC 2	3	mm	UL 746A
PLC 3	1.5	mm	UL 746A
High current arc ignition (HAI)
PLC 0	3	mm	UL 746A
PLC 1	1.5	mm	UL 746A
Compared to Leakage Traceability Index (UL)
PLC	3	PLC Code	UL 746A
M	150	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
UL flame retardant rating
94V-2	≥1.5	mm	UL 94
94-5VA	≥3	mm	UL 94
UV, water irradiation/soaking	F1		UL 746C
Igniting temperature of the hot wire
1.5 mm	825	°C	IEC 60695-2-13
Igniting temperature of the hot wire
1.5 mm	960	℃	IEC 60695-2-12

Process Conditions
Injection molding	Nominal value	Unit	Test method
drying temperature	120	°C
Drying time	3 – 4	Hrs
Drying time (cumulative)	48	Hrs
Maximum moisture content	0.02	%
Melt Temperature	295 – 315	°C
Nozzle temperature	290 – 310	°C
Front temperature	295 – 315	°C
Mid section temperature	280 – 305	°C
Post stage temperature	料斗温度	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.