| LNP FARADEX DS0036I is a compound based on Polycarbonate resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, High Impact, Non-Brominated & Non-Chlorinated Flame Retardant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Conductive,Halogen free,Flame Characteristics,EMI,RFI,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.50 | % | ISO 294-4 |
| MD：24 hrs | 0.40 to 0.70 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 55.0 | MPa | ISO 527-2 |
| yield | 57.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 4.0 to 8.0 | % | ISO 527-2 |
| yield | 3.8 | % | ISO 527-2 |
| Bending modulus | 2600 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1800 | J/m | ASTM D4812 |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| 23℃ | 120 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 85 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 125 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 136 | ℃ | ISO 75-2/Bf |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 5.6E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Shielding effectiveness | |||
| 3.00 mm | 40 to 55 | dB | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 2.10 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 293 to 304 | °C | |
| Barrel middle temperature | 310 to 321 | °C | |
| Barrel front temperature | 321 to 332 | °C | |
| Processing (melt) temperature | 304 to 327 | °C | |
| Mold temperature | 93 to 121 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |