| About |
|---|
| Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shielding and ESD.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Halogen free,Electrostatic discharge protection,Flame Characteristics,EMI,RFI,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 12 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，10 kg | 31.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.59 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.20 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3120 | MPa | ASTM D638 |
| — | 3010 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 61.0 | MPa | ASTM D638 |
| yield | 59.5 | MPa | ISO 527-2/5 |
| fracture | 57.6 | MPa | ASTM D638 |
| fracture | 55.2 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 3.4 | % | ASTM D638 |
| yield | 3.2 | % | ISO 527-2/5 |
| fracture | 3.7 | % | ASTM D638 |
| fracture | 4.4 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 2970 | MPa | ASTM D790 |
| — | 3100 | MPa | ISO 178 |
| bending strength | |||
| — | 102 | MPa | ISO 178 |
| Yield, 50 mm span | 95.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.1 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 43 | J/m | ASTM D256 |
| 23℃ | 55 | J/m | ASTM D256 |
| -30℃ | 5.7 | kJ/m² | ISO 180-1A |
| 23℃ | 5.8 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -30℃ | 590 | J/m | ASTM D4812 |
| 23℃ | 690 | J/m | ASTM D4812 |
| -30℃ | 40 | kJ/m² | ISO 180/1U |
| 23℃ | 40 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 0.180 | J | ASTM D3763 |
| — | 7.50 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 96.1 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 98.7 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 109 | ℃ | ASTM D1525, ISO 306/B50 11 16 |
| B120 | 112 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 5.7E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 6.6E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 6.4E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+7 | ohms·cm | ASTM D257 |
| Electrostatic attenuation | 10 | msec | FTMS 101B |
| Shielding effectiveness | |||
| 3.00 mm | 47 | dB | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85.0 to 90.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel rear temperature | 260 to 300 | °C | |
| Barrel middle temperature | 260 to 300 | °C | |
| Barrel front temperature | 265 to 300 | °C | |
| Nozzle temperature | 265 to 300 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 60.0 to 90.0 | °C | |
| Back pressure | 4.00 | MPa | |
| Screw speed | 30 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |