| About |
|---|
| LNP* KONDUIT* OX11315 is a thermally conductive, electrically insulative, mineral filled PPS Flame Retardant compound.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Thermal conductivity,Insulation,V-0,5VA |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.76 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 0.44 | % | ASTM D955 |
| MD：24 hrs | 0.34 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | < 0.010 | % | ISO 62 |
| 24hr，50% RH | 0.010 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 30100 | MPa | ASTM D638 |
| Tensile modulus | 18400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 54.0 | MPa | ISO 527-2/5 |
| fracture | 41.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.20 | % | ASTM D638 |
| fracture | 0.30 | % | ISO 527-2/5 |
| Bending modulus | 21400 | MPa | ISO 178 |
| 50 mm span | 26500 | MPa | ASTM D790 |
| bending strength | 84.0 | MPa | ISO 178 |
| Fracture, 50 mm span | 82.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 54 | J/m | ASTM D4812 |
| 23℃ | 16 | J/m | ASTM D256 |
| 23℃ | 1.7 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 3.9 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 5.14 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 1.14 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 238 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 242 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 275 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 275 | ℃ | ASTM D648 |
| specific heat | 1260 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | ASTM E1461 | ||
| — | 3.5 | W/m/K | ASTM E1461 |
| — | 15 | W/m/K | ASTM E1461 |
| Relative temperature index | |||
| Electrical performance | 130 | ℃ | UL 746 |
| Strength mechanical performance | 130 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.4E+15 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Recommended injection volume | 50 to 75 | % | |
| Barrel rear temperature | 316 to 343 | °C | |
| Barrel middle temperature | 316 to 343 | °C | |
| Barrel front temperature | 316 to 343 | °C | |
| Processing (melt) temperature | 321 to 349 | °C | |
| Mold temperature | 110 to 150 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 mm |
| 7. through-plane, 10*10*3 mm sample |
| 8. in-plane, 25*0.4 mm disc |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |