| About |
|---|
| White colored thermally conductive mineral filled PA6 FR compound&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Thermal conductivity,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ASTM D792 |
| Shrinkage rate | Internal Method | ||
| MD | 0.58 | % | Internal Method |
| TD | 0.53 | % | Internal Method |
| Water absorption rate | |||
| 24hr，50% RH | 0.060 | % | ASTM D570 |
| UV Weathering（Start F1 from 1mm onword） | PASSES | UL 746C | |
| Water Immersion（Start F1 from 1mm onword） | PASSES | UL 746C | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10400 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 51.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.80 | % | ASTM D638 |
| Bending modulus | |||
| 50 mm span | 11000 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 80.0 | MPa | ASTM D790 |
| Fracture, 50 mm span | 81.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 22 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 130 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 182 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 3.7E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | |||
| — | 1.5 | W/m/K | ASTM E1461 |
| — | 6.0 | W/m/K | ASTM E1461 |
| — | 0.86 | W/m/K | ISO 22007-2 |
| — | 2.7 | W/m/K | ISO 22007-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 8.1E+14 | ohms | ASTM D257 |
| Compared to the leakage tracing index | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.20 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.010 | % | |
| Barrel rear temperature | 230 to 270 | °C | |
| Barrel middle temperature | 240 to 280 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Back pressure | 0.300 to 0.900 | MPa | |
| Screw speed | 30 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |