| LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive. Also known as: LNP* KONDUIT* Compound RTF-212-11 Product reorder name: RTF2B&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | Thermal conductivity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.04 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.90 | % | ASTM D955 |
| TD：24 hrs | 1.5 | % | ASTM D955 |
| TD：24 hrs | 1.5 | % | ISO 294-4 |
| MD：24 hrs | 0.93 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr，50% RH | 0.30 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 13100 | MPa | ASTM D638 |
| — | 11900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 102 | MPa | ASTM D638 |
| fracture | 95.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.4 | % | ASTM D638 |
| fracture | 1.8 | % | ISO 527-2 |
| Bending modulus | |||
| — | 11400 | MPa | ASTM D790 |
| — | 11300 | MPa | ISO 178 |
| bending strength | |||
| — | 183 | MPa | ASTM D790 |
| — | 174 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| 23℃ | 4.7 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 450 | J/m | ASTM D4812 |
| 23℃ | 35 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 10.5 | J | ASTM D3763 |
| — | 2.00 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 226 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 216 | ℃ | ISO 75-2/Af |
| Thermal conductivity coefficient | 1.2 | W/m/K | ASTM E1530 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 282 to 293 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 93 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |