LNP™ LUBRICOMP™ 9X06030 compound

About
LNP* LUBRICOMP* 9X06030 is a compound based on PA46 resin containing PTFE and Carbon Fiber. Added features include: Internally Lubricated, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound STN-CL-4016 HS Product reorder name: 9X06030&&

Product Description
SupplierSABIC
GenericPA 46
Material StatusCommercial: Active
FeaturesLubricating,Heat Stabilized
AvailabilitysEurope
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.32g/cm³ISO 1183
Shrinkage rate
MD0.10 to 0.20%Internal Method
Water absorption rate
23℃,24hr0.040%ISO 62

MECHANICALNominal valueUnitTest method
Tensile modulus25700MPaISO 527-1-2
tensile strength
yield260MPaISO 527-2/5
Tensile strain
fracture1.5%ISO 527-2/5
Bending modulus19100MPaISO 178
bending strength359MPaISO 178
Fracture bending strain2.5%ISO 178

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch
23℃7.0kJ/m²ISO 180-1A
Notched impact strength of cantilever beam
23℃50kJ/m²ISO 180/1U

THERMALNominal valueUnitTest method
Linear coefficient of thermal expansionISO 11359-2
MD:23~60℃1.0E-51/℃
TD:23~60℃7.6E-51/℃

Electrical performanceNominal valueUnitTest method
Surface resistivity10 to 1.0E+3ohmsASTM D257

Process Conditions
injectionNominal valueUnitTest method
Drying temperature82.2°C
Drying time4.0hr
Recommended maximum moisture content0.050%
Barrel rear temperature282 to 293°C
Barrel middle temperature299 to 310°C
Barrel front temperature310 to 321°C
Processing (melt) temperature310 to 321°C
Mold temperature82.2 to 121°C
Back pressure0.172 to 0.344MPa
Screw speed30 to 60rpm

Notes
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.