| LNP™ LUBRICOMP™ Compound C2801 is a 5% PTFE reinforced PC+ABS, wear resistant, flame retardant compound for moving components in business equipment. Medium heat performance |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Lubricating,Good wear resistance,Heat Resistance, Good |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 to 0.50 | % | |
| TD：3.2 mm | 0.30 to 0.50 | % | |
| K-factor – vs Steel | 4.30E-8 | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | |||
| yield | 62.0 | MPa | |
| fracture | 51.0 | MPa | |
| Tensile strain | |||
| fracture | 110 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2720 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 95.0 | MPa | ASTM D790 |
| friction coefficient | |||
| Steel – Dynamic | 0.21 | ||
| Steel – Static | 0.16 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 82.0 | ℃ | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition (HWI) | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VB |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |