| About |
|---|
| LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 2.1 to 2.9 | % | ASTM D955 |
| TD：24 hrs | 2.1 to 2.9 | % | ASTM D955 |
| TD：24 hrs | 2.1 to 2.9 | % | ISO 294-4 |
| TD：24 hrs | 2.1 to 2.9 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr，50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.43 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 1830 | MPa | ASTM D638 |
| — | 2020 | MPa | ISO 527-1-2 |
| Tensile strength | |||
| yield | 43.0 | MPa | ASTM D638 |
| yield | 39.0 | MPa | ISO 527-2 |
| fracture | 43.0 | MPa | ASTM D638 |
| fracture | 39.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 14 | % | ASTM D638 |
| yield | 22 | % | ISO 527-2 |
| fracture | 30 | % | ASTM D638 |
| fracture | 43 | % | ISO 527-2 |
| Bending modulus | |||
| — | 2020 | MPa | ASTM D790 |
| — | 2080 | MPa | ISO 178 |
| bending strength | |||
| — | 63.0 | MPa | ASTM D790 |
| — | 60.0 | MPa | ISO 178 |
| friction coefficient | |||
| dynamic | 0.25 | ||
| static state | 0.14 | ||
| Wear factor | 1.8E+6 | 10^-8 mm³/N·m | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 53 | J/m | ASTM D256 |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 620 | J/m | ASTM D4812 |
| 23℃ | 42 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23°C，Energy at Peak | 3.00 | J | ASTM D3763 |
| — | 1.00 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 87.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 79.0 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| TD：-40℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Temperature at the rear of the barrel | 175 to 190 | °C | |
| Temperature in the middle of the barrel | 195 to 205 | °C | |
| Front temperature of material barrel | 210 to 220 | °C | |
| Processing (melt) temperature | 200 to 215 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |