| About |
|---|
| LNP* LUBRICOMP* DCI06APW is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, High Flow.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Conductive |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 300℃，5 kg | 28.0 | cm³/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 0.050 to 0.15 | % | |
| TD：24 hrs | 0.15 to 0.40 | % | |
| Water absorption rate | |||
| 24hr，50% RH | 0.11 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 25400 | MPa | ASTM D638 |
| — | 23800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 183 | MPa | ASTM D638 |
| fracture | 183 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.4 | % | ASTM D638 |
| fracture | 1.6 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 20100 | MPa | ASTM D790 |
| — | 20600 | MPa | ISO 178 |
| bending strength | |||
| — | 262 | MPa | ISO 178 |
| Fracture, 50 mm span | 265 | MPa | ASTM D790 |
| compressive strength | 128 | MPa | Internal Method |
| shear modulus | 3510 | MPa | ASTM C273 |
| shear strength | 92.0 | MPa | ASTM C273 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 94 | J/m | ASTM D256 |
| 23℃ | 9.3 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 500 | J/m | ASTM D4812 |
| 23℃ | 34 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 16.8 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 128 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 130 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-30~30℃ | 9.7E-6 | 1/℃ | |
| TD：-30~30℃ | 4.6E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+3 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 270 to 285 | °C | |
| Barrel middle temperature | 275 to 290 | °C | |
| Barrel front temperature | 285 to 300 | °C | |
| Mold temperature | 100 to 120 | °C | |
| Back pressure | 0.200 to 0.300 | MPa | |
| Screw speed | 40 to 80 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |