| About |
|---|
| LNP LUBRICOMP EX03599H is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.80 | % | ASTM D955 |
| MD：24 hrs | 0.70 | % | ASTM D955 |
| TD：24 hrs | 0.78 | % | ISO 294-4 |
| MD：24 hrs | 0.72 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| 24hr，50% RH | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3340 | MPa | ASTM D638 |
| Tensile modulus | 3190 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 98.0 | MPa | ISO 527-2 |
| fracture | 88.9 | MPa | ASTM D638 |
| yield | 106 | MPa | ISO 527-2 |
| yield | 105 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 28 | % | ASTM D638 |
| fracture | 9.7 | % | ISO 527-2 |
| yield | 6.8 | % | ISO 527-2 |
| yield | 7.0 | % | ASTM D638 |
| Bending modulus | 3480 | MPa | ASTM D790 |
| Bending modulus | 3140 | MPa | ISO 178 |
| bending strength | 152 | MPa | ASTM D790 |
| bending strength | 112 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.44 | ASTM D3702 Modified | |
| static state | 0.45 | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1400 | J/m | ASTM D4812 |
| 23℃ | 48 | J/m | ASTM D256 |
| 23℃ | 5.9 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 90 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 6.88 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 2.56 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 187 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 190 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 4.2E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 4.1E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 4.4E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 4.3E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 343 to 354 | °C | |
| Barrel middle temperature | 354 to 366 | °C | |
| Barrel front temperature | 366 to 377 | °C | |
| Processing (melt) temperature | 360 to 366 | °C | |
| Mold temperature | 121 to 149 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type 1A |
| 4. Modified: Manual |
| 5. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |