| About |
|---|
| LNP™ LUBRICOMP™ EX06405 compound LNP LUBRICOMP EX06405 is a compound based on Polyetherimide resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible, Easy Molding. Also known as: LNP* LUBRICOMP* Compound EFL-4034 EM LE Product reorder name: EX06405&&LNP™ LUBRICOMP™ EX06405 compound LNP LUBRICOMP EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. Also known as: LNP* LUBRICOMP* Compound EFL-4034 EM LE Product reorder name: EX06405&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low extract,Lubricating,Good wear resistance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ASTM D792 |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.40 to 0.60 | % | ASTM D955 |
| MD：24 hrs | 0.30 to 0.50 | % | ASTM D955 |
| TD：24 hrs | 0.51 | % | ISO 294-4 |
| MD：24 hrs | 0.42 | % | ISO 294-4 |
| Water absorption rate | |||
| 24hr，50% RH | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7580 | MPa | ASTM D638 |
| Tensile modulus | 7140 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 119 | MPa | ISO 527-2 |
| fracture | 123 | MPa | ASTM D638 |
| yield | 123 | MPa | ASTM D638 |
| yield | 119 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.4 | % | ASTM D638 |
| fracture | 2.5 | % | ISO 527-2 |
| yield | 2.4 | % | ASTM D638 |
| yield | 2.5 | % | ISO 527-2 |
| Bending modulus | 6890 | MPa | ASTM D790 |
| Bending modulus | 6900 | MPa | ISO 178 |
| bending strength | 152 | MPa | ASTM D790 |
| bending strength | 169 | MPa | ISO 178 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.44 | ASTM D3702 Modified | |
| static state | 0.52 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 69.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 7.7 | kJ/m² | ISO 180-1A |
| 23℃ | 490 | J/m | ASTM D4812 |
| 23℃ | 69 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 31 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 11.8 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 3.70 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 204 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 202 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 211 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 209 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 3.6E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 3.7E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.5E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.6E-5 | 1/℃ | ASTM E831 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 343 to 354 | °C | |
| Barrel middle temperature | 354 to 366 | °C | |
| Barrel front temperature | 366 to 377 | °C | |
| Processing (melt) temperature | 360 to 366 | °C | |
| Mold temperature | 121 to 149 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 60 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |