| About |
|---|
| LNP LUBRICOMP* FX04491H is a compound based on Polyethylene resin containing Proprietary Fillers. Added features of this material include: Wear Resistant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.932 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：24 hrs | 1.6 | % | ASTM D955 |
| MD：24 hrs | 2.4 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 24.5 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 7.4 | % | ASTM D638 |
| Bending modulus | 10700 | MPa | ASTM D790 |
| bending strength | 23.4 | MPa | ASTM D790 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.13 | ASTM D3702 Modified | |
| static state | 0.11 | ASTM D3702 Modified | |
| Wear factor | |||
| Washer | 24.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ASTM D4812 | |
| 23℃ | 46 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 42.2 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 193 to 204 | °C | |
| Barrel middle temperature | 210 to 221 | °C | |
| Barrel front temperature | 221 to 232 | °C | |
| Processing (melt) temperature | 232 | °C | |
| Mold temperature | 38 to 54 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1A |
| 3. Modified: Manual |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |