| LNP LUBRICOMP OFL36 is a compound based on PPS – Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Excellent Processability |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.69 | g/cm³ | ASTM D792 |
| Density | 1.70 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.60 to 0.80 | % | ASTM D955 |
| MD：24 hrs | 0.10 to 0.20 | % | ASTM D955 |
| TD：24 hrs | 0.30 to 0.48 | % | ISO 294-4 |
| MD：24 hrs | 0.13 to 0.18 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.010 | % | ISO 62 |
| 24hr，50% RH | 1.2E-3 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12800 | MPa | ASTM D638 |
| Tensile modulus | 12000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 121 | MPa | ISO 527-2/5 |
| fracture | 124 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.3 | % | ISO 527-2/5 |
| fracture | 1.3 | % | ASTM D638 |
| Bending modulus | 11100 | MPa | ISO 178 |
| 50 mm span | 11600 | MPa | ASTM D790 |
| bending strength | 180 | MPa | ISO 178 |
| Fracture, 50 mm span | 178 | MPa | ASTM D790 |
| friction coefficient | ASTM D3702 Modified | ||
| dynamic | 0.44 | ASTM D3702 Modified | |
| static state | 0.35 | ASTM D3702 Modified | |
| Wear factor | ASTM D3702 Modified | ||
| Ring | 7.00 to 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 52.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | J/m | ASTM D256 |
| 23℃ | 5.7 | kJ/m² | ISO 180-1A |
| 23℃ | 420 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 25 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| 23℃，Energy at Peak Load | 3.40 | J | ASTM D3763 |
| 23℃，Total Energy | 11.8 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 2.30 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 257 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 264 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 278 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 278 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831 |
| TD：-30~30℃ | 3.4E-5 | 1/℃ | ASTM D696 |
| MD：-40~40℃ | 2.4E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 2.3E-5 to 5.0E-5 | 1/℃ | ASTM E831 |
| MD：-30~30℃ | 2.5E-5 | 1/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 to 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 304 to 316 | °C | |
| Barrel middle temperature | 321 to 332 | °C | |
| Barrel front temperature | 332 to 343 | °C | |
| Processing (melt) temperature | 316 to 321 | °C | |
| Mold temperature | 138 to 166 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Modified: Manual |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |