| About |
|---|
| LNP* Lubricomp* Compound PFL34是基于含有玻璃纤维和PETF的尼龙6树脂的化合物。此材料的突出性能是自润滑性。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Self-lubricating,Self-extinguishing,Good wear resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Fracture, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
| Fracture, 5 mm/min | 138 | MPa | ISO 527 |
| fracture | 130 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 5 mm/min | 3.2 | % | ASTM D638 |
| Fracture, 5 mm/min | 3.2 | % | ISO 527 |
| fracture | 3.1 | % | ASTM D638 |
| bending strength | 1750 | kgf/cm² | ASTM D 790 |
| Fracture, 1.30 mm/min, 50 mm span | 212.877 | MPa | ASTM D790 |
| Yield, 1.30 mm/min, 50 mm span | 213.858 | MPa | ASTM D790 |
| Bending modulus | 52700 | kgf/cm² | ASTM D 790 |
| 2 mm/mim | 6750 | MPa | ISO 178 |
| 1.3 mm/min，50mm跨距 | 6994.53 | MPa | ASTM D790 |
| Tensile modulus | |||
| 5 mm/min | 7906.86 | MPa | ASTM D638 |
| 50 mm/min | 7563.51 | MPa | ASTM D638 |
| 1 mm/min | 8230 | MPa | ISO 527 |
| bending strength | 209 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 960.4 | J/m | ASTM D4812 |
| 23℃ | 862.4 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 98 | J/m | ASTM D256 |
| 23℃ | 127.4 | J/m | ASTM D256 |
| Total energy of instrument impact | 91 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 202 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 209 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 219 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-30~30℃ | 7.E-07 | 1/℃ | ASTM D696 |
| MD：-30~30℃ | 3.1E-06 | 1/℃ | ASTM D696 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.4 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr，50% RH | 0.89 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：24 hrs | 0.6-0.8 | % | ASTM D955 |
| MD：24 hrs | 0.2-0.4 | % | ASTM D955 |
| MD：24 hrs | 0.3 | % | ASTM D955 |
| Factors of gasket wear | 29 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Environmental wear factors | 3 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic friction coefficient | 0.46 | – | ASTM D 3702 Modified |
| Static friction coefficient | 0.51 | – | ASTM D 3702 Modified |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 80 | ℃ | |
| Irritable time | 4 | hrs | |
| Maximum water absorption | 0.15-0.25 | % | |
| Melt temperature | 265-275 | ℃ | |
| Front temperature | 275-290 | ℃ | |
| Mid section temperature | 265-275 | ℃ | |
| Post stage temperature | 250-260 | ℃ | |
| Grinding tool temperature | 80-95 | ℃ | |
| Back pressure | 0.3-0.7 | MPa | |
| Screw speed | 30-60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |