| About |
|---|
| LNP™ LUBRICOMP™ PFL36 compound LNP LUBRICOMP PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PFL-4036 Product reorder name: PFL36&&LNP™ LUBRICOMP™ PFL36 compound LNP LUBRICOMP PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound PFL-4036 Product reorder name: PFL36&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8270 | MPa | ASTM D638 |
| Tensile modulus | 7880 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 113 | MPa | ISO 527-2 |
| fracture | 110 | MPa | ASTM D638 |
| yield | 110 | MPa | ASTM D638 |
| yield | 113 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 4.5 | % | ISO 527-2 |
| fracture | 6.7 | % | ASTM D638 |
| yield | 5.8 | % | ASTM D638 |
| yield | 4.1 | % | ISO 527-2 |
| Bending modulus | 5520 | MPa | ASTM D790 |
| Bending modulus | 7000 | MPa | ISO 178 |
| bending strength | 172 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 1100 | J/m | ASTM D4812 |
| 23℃ | 17 | kJ/m² | ISO 180-1A |
| 23℃ | 150 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 79 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 19.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 202 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 201 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 216 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 216 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 249 to 260 | °C | |
| Barrel middle temperature | 266 to 277 | °C | |
| Barrel front temperature | 277 to 288 | °C | |
| Processing (melt) temperature | 266 to 277 | °C | |
| Mold temperature | 82 to 93 | °C | |
| Back pressure | 0.344 to 0.689 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |