| About |
|---|
| LNP LUBRICOMP RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4522 Product reorder name: RAP22&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，50% RH | 1.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 71 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 6.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 3430 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 103 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 3260 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 224 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 100 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD | 4.9E-5 | 1/℃ | ISO 11359-2 |
| TD | 8.7E-5 | 1/℃ | ISO 11359-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 25 | kJ/m² | ISO 180/1U |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4 | Hr | |
| Water content | 0.15-0.25 | % | |
| Injection temperature | |||
| Rear barrel temperature | 265-275 | °C | |
| Central temperature of the barrel | 285-295 | °C | |
| Barrel front temperature | 295-305 | °C | |
| Mold temperature | 85-95 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |