| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,Good wear resistance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ASTM D792 |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 24hr | 0.60 | % | ASTM D570 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.011 to 0.012 | % | ISO 294-4 |
| MD：24 hrs | 0.003 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11200 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 139 | MPa | ASTM D638 |
| yield | 139 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.1 | % | ASTM D638 |
| yield | 2.1 | % | ASTM D638 |
| friction coefficient | ASTM D3702 | ||
| dynamic | 0.59 | ASTM D3702 | |
| static state | 0.43 | ASTM D3702 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 10.4 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 51.4 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃ | 10.6 | J | ASTM D3763 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Processing (melt) temperature | 280 to 302 | °C | |
| Mold temperature | 93.3 to 107 | °C | |
| Back pressure | 0.172 to 0.345 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |