| About |
|---|
| LNP™ LUBRICOMP™ RFL36 compound LNP LUBRICOMP RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound RFL4036 Product reorder name: RFL36&&LNP™ LUBRICOMP™ RFL36 compound LNP* Lubricomp* RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound RFL4036 Product reorder name: RFL36&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,HB |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 15.0 to 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.44 | % | |
| MD：24 hrs | 0.050 | % | |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 1.3 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.46 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 166 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.6 | % | ISO 527-2/5 |
| Bending modulus | ISO 178 | ||
| — | 7200 | MPa | |
| 60℃ | 5300 | MPa | |
| 100℃ | 4200 | MPa | |
| 150℃ | 3500 | MPa | |
| 200℃ | 3100 | MPa | |
| bending strength | ISO 178 | ||
| — | 234 | MPa | |
| — | 277 | MPa | |
| 60℃ | 179 | MPa | |
| 100℃ | 131 | MPa | |
| 150℃ | 96.0 | MPa | |
| 200℃ | 83.0 | MPa | |
| friction coefficient | |||
| With oneself – dynamic | 0.59 | ASTM D3702 | |
| Fracture bending strain | ISO 178 | ||
| — | 4.1 | % | |
| 60℃ | 6.1 | % | |
| 100℃ | 6.6 | % | |
| 150℃ | 5.6 | % | |
| 200℃ | 6.3 | % | |
| Wear factor | |||
| Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 12 | kJ/m² | |
| 23℃ | 16 | kJ/m² | |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -40℃ | 74 | kJ/m² | |
| 23℃ | 84 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | > 220 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | > 220 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 2.5E-5 | 1/℃ | |
| TD：23~60℃ | 7.5E-5 | 1/℃ | |
| specific heat | 1990 | J/kg/℃ | ASTM E1269 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM D5930 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 282 to 293 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 93.3 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |