| Zythane 5050D is a polyester--based TPU specifically formulated for extrusion applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability, oil, fuel and solvent resistance. It is supplied uncolored in pellet form. Typical Applications: Zythane 5050D applications include among others spiral and pneumatic tubing, round and V belting, blow molded bellows.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Good wear resistance,Grease resistance,Solvent resistance,Fuel resistance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：24 hrs | 0.60 | % | ASTM D955 |
| TD | 1.5 | % | Internal Method |
| Water absorption rate | |||
| 24hr，50% RH | 0.69 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.47 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 10200 | MPa | ASTM D638 |
| — | 10300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 150 | MPa | ASTM D638 |
| fracture | 150 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.3 | % | ASTM D638 |
| fracture | 2.4 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 9660 | MPa | ASTM D790 |
| — | 9140 | MPa | ISO 178 |
| bending strength | |||
| — | 214 | MPa | ISO 178 |
| Fracture, 50 mm span | 219 | MPa | ASTM D790 |
| friction coefficient | ASTM D3702 Modified | ||
| With oneself – dynamic | 0.52 | ||
| With oneself – static | 0.50 | ||
| Wear factor | ASTM D3702 Modified | ||
| Ring | 3.90 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 27.0 | 10^-10 in^5-min/ft-lb-hr |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 100 | J/m | ASTM D256 |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 750 | J/m | ASTM D4812 |
| 23℃ | 52 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 7.48 | J | ASTM D3763 |
| — | 2.20 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 261 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 259 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 253 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 249 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-30~30℃ | 2.5E-5 | 1/℃ | |
| TD：-30~30℃ | 5.6E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82.2 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.15 to 0.25 | % | |
| Barrel rear temperature | 266 to 277 | °C | |
| Barrel middle temperature | 282 to 293 | °C | |
| Barrel front temperature | 293 to 304 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 93.3 to 110 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |